|Material:||MT302,MT304,MT304L 316L||Standard:||A511 Or 511M|
|Application:||Mechanical Applications||Surface Treatment:||Varnish, Oil-dip, Passivation...|
|Delivery Status:||Annealed, Normalized, Normalized+Tempered...||Package:||Bundles/Pallets/Weave Stip|
ASTM A511 SS Tubing,
MT304 SS Tubing,
6.35mm SS Tubing
SS Tubing ASTM A511 / A511M MT304 316L Standard
ASTM A511/A511M specification covers seamless stainless tubing for use in mechanical applications where corrosion-resistant or high-temperature strength is needed.
Chemical Composition :
|Grade||Chemical Composition %|
|C||Mn max||P max||S max||Si max||Ni||Cr||Mo||Ti||Nb&Ta||Se|
|MT 304||0.08 max||2||0.04||0.03||1||8-11||18-20||...||...||...||...|
|MT 304L||0.035 max||2||0.04||0.03||1||8-13||18-20||...||...||...||...|
|MT 316||0.08 max||2||0.04||0.03||1||11-14||16-18||2-3||...||...||...|
|MT 316L||0.035 max||2||0.04||0.03||1||10-15||16-18||2-3||...||...||...|
|MT 317||0.08 max||2||0.04||0.03||1||11-14||18-20||3-4||...||...||...|
|MT 347||0.08 max||2||0.04||0.03||1||9-13||17-20||...||...||...||...|
Mark: As required.
Inspection and Test: chemical composition test, mechanical properties test(tensile, yield, elongation), process properties test(flatting, flaring, bending, hardness, impact, etc.), appearance and size test, non-destructive inspection test, hydrostastic test.
Delivery status: Annealed, normalized, normalized+Tempered, etc.
Surface treatment: oil impregnation, paint, passivation, phosphating, shot blasting etc.
Packing: Exporting package/wooden box /as requirement.
This specification covers seamless stainless steel tubing for use in mechanical applications where corrosion-resistant or high-temperature strength is needed. The steel may be cast in ingots or may be strand cast. When steel of different grades is sequentially strand cast, identification of the resultant transition material is required. The tubes shall be made by a seamless process and by either cold working or hot working as specified. Seamless stainless steel tubing is a tubular product made without a welded seam. It is usually manufactured by hot working steel and then cold finishing the hot-worked tubing to produce the desired shape, dimensions and properties All austenitic tubes shall be furnished in the annealed condition. An analysis of each heat of steel shall be made to determine the percentages of the elements specified. If secondary melting processes are employed, the heat analysis shall be obtained from one remelted ingot or the product of one remelted ingot of each primary melt.
Contact Person: Mrs. Yana Dong
Tel: 13661003712, 86-10-5712 1108, 5718 5998